降低放熱熔焊焊接點(diǎn)缺陷率
劉學(xué)軍1，鄭燁2，李金華2，謝玖榮2
1 國(guó)網(wǎng)山東省電力公司濰坊供電公司，山東 濰坊 261000； 2 國(guó)網(wǎng)湖南省送變電工程公司，湖南 長(zhǎng)沙 410007
摘 要：針對(duì)變電工程中放熱熔焊焊接點(diǎn)缺陷率高的現(xiàn)象，從焊接模具、焊接材料、焊接工藝等方面分析研究了其產(chǎn)生原因，并對(duì)主要末端原因制定相對(duì)應(yīng)的措施，經(jīng)九江500 kV 變電站新建工程中推廣實(shí)施，該相關(guān)方法及措施有效降低了放熱熔焊焊接點(diǎn)缺陷率。
關(guān)鍵詞：放熱熔焊；變電工程；接地網(wǎng)；缺陷率
中圖分類號(hào)：TG441.7；TM862 文獻(xiàn)標(biāo)識(shí)碼：B 文章編號(hào)：1007-3175(2015)12-0047-03
How to Reduce Defect Rate of Exothermic Fusion Welding Point
LIU Xue-jun1, ZHENG Ye2, LI Jin-hua2, XIE Jiu-rong2
1 State Grid Shandong Electric Power Company Weifang Power Supply Company, Weifang 261000, China; 2 State Grid Hunan Electric Power Transmission & Transformation Engineering Company, Changsha 410007, China
Abstract: Aiming at the phenomenon that the exothermic fusion welding point had high defect rate in power transformation engineering,this paper analyzed the causes from the aspects of welding mould, welding material and welding technology and enacted the corresponding measures for the main terminals. After the generalized implementation in the new construction of Jiujiang 500 kV power transformation engineering,this correlation method and measures reduce the defect rate of exothermic fusion welding point.
Key words: exothermic fusion welding; power transformation engineering; grounding grid; defect rate
參考文獻(xiàn)
[1] 呂志寧，郭宏偉. 銅鍍鋼接地線放熱焊接在變電站接地中的應(yīng)用[J].科學(xué)之友，2011(7)：5-6.
[2] 劉波. 銅鋼復(fù)合材料和放熱焊接技術(shù)在石油化工企業(yè)接地系統(tǒng)中的應(yīng)用[J].中國(guó)新技術(shù)新產(chǎn)品，2011(8)：14.
[3] 龔寧. 放熱焊技術(shù)在菲律賓電網(wǎng)接地施工中的應(yīng)用[J]. 電力與能源，2012，33(6)：620-622.
[4] 魏常信，關(guān)金鎖.WTWELD放熱焊接工藝在電網(wǎng)直流工程接地設(shè)施中的應(yīng)用[J].中國(guó)新技術(shù)新產(chǎn)品，2010(14)：140-141.
[5] 王鵬. 水電站永久接地網(wǎng)的放熱焊接工藝[J]. 水利水電施工，2008(3)：62-64.
[6] 王云琪，曹翔宗，袁陽(yáng). 放熱焊接工藝在綜合接地工程中的應(yīng)用研究[J].中國(guó)西部科技，2014，13(10)：42.